Decreasing thermal stresses in steam generator collector welds area using external cooling

KRAUTSCHNEIDER, R. JOCH, L.

Czech title

Snížení tepelného namáhání kolektorů parogenerátoru v oblasti svarového spoje pomocí externího chlazení

English title

Decreasing thermal stresses in steam generator collector welds area using external cooling

Type

conference paper

Language

en

Original abstract

Presented paper deals with possibility of external cooling of steam generator welds area to decrease internal tensile thermal stresses which are one of the causes of cracking in this area. On various WWER-440 nuclear power plants (NPP) steam generators (SG) occurred quite serious problem of cracking in weld joints connecting primary collectors to the SG vessels nozzle. The cause of this cracking is stress corrosion cracking (SCC) mechanism. Results of these analyses showed that by proper external cooling of the weld area it is possible not just to decrease significantly existing tensile stresses, but to change them into compressive ones. This of course would have great impact on crack occurrence and growth.

Czech abstract

Uvedený článek se zabývá možností vnějšího chlazení kolektoru parního generátoru v oblasti svaru, za účelem snížení tahového napětí od teploty, které jsou jednou z příčin vzniku trhlin v této oblasti. Na různých jaderných elektrárnách typu VVER-440 se vyskytly poměrně závažné vady spojené se vznikem trhlin ve svarovém spoji spojujícím primární kolektory s nátrubky parního generátoru. Příčinou těchto trhlin je mechanizmus korozního praskání pod napětím (SCC). Výsledky těchto analýz ukazují, že vhodným vnějším chlazením svaru je možné nejen výrazně snížit existující tahové napětí, ale dokonce je změnit v tlakové. To samozřejmě bude mít velký vliv na vznik trhlin a jejich další šíření.

English abstract

Presented paper deals with possibility of external cooling of steam generator welds area to decrease internal tensile thermal stresses which are one of the causes of cracking in this area. On various WWER-440 nuclear power plants (NPP) steam generators (SG) occurred quite serious problem of cracking in weld joints connecting primary collectors to the SG vessels nozzle. The cause of this cracking is stress corrosion cracking (SCC) mechanism. Results of these analyses showed that by proper external cooling of the weld area it is possible not just to decrease significantly existing tensile stresses, but to change them into compressive ones. This of course would have great impact on crack occurrence and growth.

Keywords in Czech

parogenerátor; teplotní namáhání; vnější chlazení; korozní praskání pod napětím; heterogení svarový spoj

Keywords in English

steam generator; thermal stresses; external cooling; stress corrosion cracking; dissimilar metal weld

RIV year

2014

Released

05.05.2016

Publisher

Elsevier

ISSN

2211-8128

Book

Procedia Materials Science

Volume

12

Number

1

Pages from–to

12–17

Pages count

6

BIBTEX


@inproceedings{BUT109173,
  author="Roman {Krautschneider} and Lukáš {Joch},
  title="Decreasing thermal stresses in steam generator collector welds area using external cooling",
  booktitle="Procedia Materials Science",
  year="2016",
  volume="12",
  number="1",
  month="May",
  pages="12--17",
  publisher="Elsevier",
  issn="2211-8128"
}