Publication detail

MECHANICAL ALLOYING OF 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si SOFT MAGNETIC PERMALLOY TYPE MATERIAL

HADRABA, H. HUSÁK, R. ROUPCOVÁ, P.

Czech title

Mechanické legování magneticky měkké slitiny 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si

English title

MECHANICAL ALLOYING OF 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si SOFT MAGNETIC PERMALLOY TYPE MATERIAL

Type

journal article - other

Language

en

Original abstract

80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic alloy of Permalloy type was prepared by mechanical alloying from atomic powders. The powders were mechanically alloyed by high-energy ball milling in a planetary mill in an air atmosphere. Comparing results from electron energy chemical analysis and X-ray diffraction analysis it was found that hardness of the alloy corresponds to the chemical and phase homogeneity of the composite powder. After 24 hours of milling, the single phase homogenous composite powder had the Vickers hardness of about 750 HV1 and coercivity about 40 A.m-1. Further alloying led to powder grain size and crystallinite size refinement. This process was accompanied by an increase in the defects amount and thus with increasing of coercivity, up to 120 A.m-1 after alloying for 120 hours. Keywords: soft magnetic materials, Permalloy, mechanical alloying

Czech abstract

Magneticky měkká slitina typu Permalloy 80Ni-14,7Fe-4,4Mo-0,5Mn-0,3Si byla připravena pomocí techniky mechanického legování z atomárně čistých prášků. Prášky byly zpracovávány pomocí vysoko-energetických kulových mlýnů planetového typu ve vzdušné atmosféře. Srovnáním výsledků z chemických analýz a rentgenových analýz byla zjištěna tvrdost, které odpovídá jak chemické homogenitě, tak také homogenitě fázového složení kompozitního prášku. Po 24 hodinách mletí je přítomna již jen jediná homogení fáze kompozitního prášku, která má tvrdost měřenou metodou podle Vickerse kolem 750 HV1 a koercitivní sílu kolem 40A/m. S pokračujícím mechanickým legováním dochází již pouze ke zjemňování velikosti prachových zrn a krystalitů. Proces zjemňování zrn je doprovázen zvýšením počtu defektů z důvodu silné plastické deformace a to má za následek zvýšení koercitivní síly až na 120A/m po 120 hodinách mechanického legování.

English abstract

80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic alloy of Permalloy type was prepared by mechanical alloying from atomic powders. The powders were mechanically alloyed by high-energy ball milling in a planetary mill in an air atmosphere. Comparing results from electron energy chemical analysis and X-ray diffraction analysis it was found that hardness of the alloy corresponds to the chemical and phase homogeneity of the composite powder. After 24 hours of milling, the single phase homogenous composite powder had the Vickers hardness of about 750 HV1 and coercivity about 40 A.m-1. Further alloying led to powder grain size and crystallinite size refinement. This process was accompanied by an increase in the defects amount and thus with increasing of coercivity, up to 120 A.m-1 after alloying for 120 hours. Keywords: soft magnetic materials, Permalloy, mechanical alloying

Keywords in Czech

Mechanické legování, magneticky měkké slitiny, permalloy

Keywords in English

Mechanical alloying, Soft magnetic material, Permalloy

RIV year

2014

Released

03.09.2014

ISSN

1335-8987

Volume

14

Number

4

Pages from–to

208–214

Pages count

7

BIBTEX


@article{BUT115418,
  author="Hynek {Hadraba} and Roman {Husák} and Pavla {Roupcová} and Magdaléna {Strečková},
  title="MECHANICAL ALLOYING OF 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si SOFT MAGNETIC PERMALLOY TYPE MATERIAL",
  year="2014",
  volume="14",
  number="4",
  month="September",
  pages="208--214",
  issn="1335-8987"
}