Vliv superponovaného normálového napětí na teoretickou smykovou pevnost v bcc kovech

Influence of Superimposed Normal Loading on the Shear Strength in bcc Metals

conference paper

en

The influence of stress applied perpendicularly to a slip plane during shear deformation of a crystal on the shear strength is important in many deformation processes. As an example, one can consider a nanoindentation process as a combination of shear and compressive deformations in the vicinity of an indentor. Previous studies, based on the empirical Lennard- Jones potential, suggested nearly linear dependence of the theoretical shear strength on the normal tensile and compressive loading. The aim of this study is to verify those results using an ab initio approach for bcc Nb, Mo and W. The three bcc crystals were subjected to shear deformations in <111>{112} slip system. Linear dependence was confirmed.

Vliv napětí aplikovaného kolmo ke skluzové rovině v průběhu smykové deformace krystalu na teoretickou smykovou pevnost je důležitý v mnoha deformačních procesech. Jako příklad lze uvažovat nanoindentační proces jako kombinaci smykové a tlakové deformace v okolí indentoru. Předchozí studie založené na Lennard-Jonesových potenciálech naznačovaly téměř lineární závislost teoretické smykové pevnosti na normálovém tahovém a tlakovém zatěžování. Cílem této studie je ověřit tyto výsledky s užitím ab initio přístupu pro bcc Nb, Mo a W. Tyto tři bcc krystaly byly podrobeny smyku v <111>{112} skluzovém systému. Lineární závisost byla potvrzena.

The influence of stress applied perpendicularly to a slip plane during shear deformation of a crystal on the shear strength is important in many deformation processes. As an example, one can consider a nanoindentation process as a combination of shear and compressive deformations in the vicinity of an indentor. Previous studies, based on the empirical Lennard- Jones potential, suggested nearly linear dependence of the theoretical shear strength on the normal tensile and compressive loading. The aim of this study is to verify those results using an ab initio approach for bcc Nb, Mo and W. The three bcc crystals were subjected to shear deformations in <111>{112} slip system. Linear dependence was confirmed.

Shear strength, ab initio, influence of normal stress, bcc metals.