Publication detail
Stability of microstructure of ultra fine-grained copper during cyclic loading
BUKSA, M. KUNZ, L. SVOBODA, M.
Czech title
Stabilita mikrostruktury ultrajemnozrnné mědi během cyklického zatěžování
English title
Stability of microstructure of ultra fine-grained copper during cyclic loading
Type
conference paper
Language
en
Original abstract
Fatigue properties, microstructural changes and strain localization in ultrafine-grained copper produced by equal channel angular pressing technique has been experimentally studied. The cyclic stress-strain response under stress control depends on the stress amplitude. The formation of shear bands resulting in fatigue crack initiation was observed both for low and high stress amplitudes.
Czech abstract
Experimentálně byly studovány únavové vlastnosti, mikrostrukturní změny a lokalizace deformace v ultrajemnozrnné mědi vyrobené pomocí ECAP techniky. Cyklická napěťově deformační odezva ultrajemnozrnné mědi závisí na amplitudě napětí. Smykové pásy mající za následek vznik únavové trhliny byly pozorovány jak při nízké tak i při vysoké hodnotě amplitudy napětí.
English abstract
Fatigue properties, microstructural changes and strain localization in ultrafine-grained copper produced by equal channel angular pressing technique has been experimentally studied. The cyclic stress-strain response under stress control depends on the stress amplitude. The formation of shear bands resulting in fatigue crack initiation was observed both for low and high stress amplitudes.
Keywords in English
Fatigue properties; ECAP; Copper; Ultrafine-grained structure
RIV year
2005
Released
01.12.2005
Publisher
ÚFM AV ČR
Location
Brno
ISBN
80-239-6145-4
Book
Víceúrovňový design pokrokových materiálů
Pages from–to
131–138
Pages count
8
BIBTEX
@inproceedings{BUT21729,
author="Michal {Buksa} and Ludvík {Kunz} and Milan {Svoboda},
title="Stability of microstructure of ultra fine-grained copper during cyclic loading",
booktitle="Víceúrovňový design pokrokových materiálů",
year="2005",
month="December",
pages="131--138",
publisher="ÚFM AV ČR",
address="Brno",
isbn="80-239-6145-4"
}