The effect of electromagnetic (i.e. induction) stirring of the melt of concast billets on the reduction of their surface defects

STRÁNSKÝ, K. KAVIČKA, F. ŠTĚTINA, J. SEKANINA, B. STRÁNSKÝ, L.

Czech title

Vliv elektromagnetického míchání taveniny konttinuálně litých sochorů na snížení jejich povrchových vad

English title

The effect of electromagnetic (i.e. induction) stirring of the melt of concast billets on the reduction of their surface defects

Type

conference paper

Language

en

Original abstract

Electromagnetic stirring (EMS) suppresses the growth of columnar crystals of billets and reduces the tendency to cracking during casting and at low temperatures. A caster was used for the testing of two induction stirrers – one on the actual mould and the other beneath the mould – to determine the effect of EMS on the formation of the structure of non-alloy steel. Experimental research was also confronted with results acquired from the application of the models of the temperature field and chemical heterogeneity and the physical-similarity theory. Statistical monitoring of the quality of concast billets has proven that stirring significantly reduces the occurrence of defects – in this case cracks.

Czech abstract

Elektromagnetické míchání potlačuje růst sloupcovitých krystalů v sochorech a snižuje tendenci k tvorbě trhlin při odlévání a nízkých teplotách. Licí stroj byl použit pro testování dvou indukčních míchačů – na krystalizátoru a pod krystalizátorem- pro stanovení účinku míchání na tvorbu struktury nelegované oceli. Experimentální výzkum byl srovnán s výsledky aplikace modelů teplotního pole a chemické heterogenity a teorie fyzikální podobnosti. Statistické vyhodnocení kvality sochorů prokázalo, že míchání významně snižuje výskyt defektů – v tomto případě trhlin.

English abstract

Electromagnetic stirring (EMS) suppresses the growth of columnar crystals of billets and reduces the tendency to cracking during casting and at low temperatures. A caster was used for the testing of two induction stirrers – one on the actual mould and the other beneath the mould – to determine the effect of EMS on the formation of the structure of non-alloy steel. Experimental research was also confronted with results acquired from the application of the models of the temperature field and chemical heterogeneity and the physical-similarity theory. Statistical monitoring of the quality of concast billets has proven that stirring significantly reduces the occurrence of defects – in this case cracks.

Keywords in Czech

kontinuální lití, elektromagnetické míchání, dendritická struktura, kvalita sochorů, vady

Keywords in English

concasting, electromagnetic stirring, dendritic structure, quality of billets, defects.

RIV year

2008

Released

02.09.2008

Publisher

VUTIUM Brno

Location

Brno

ISBN

9781617823190

Book

Proceedings of ECF 17

Pages from–to

196–196

Pages count

1

BIBTEX


@inproceedings{BUT26741,
  author="Karel {Stránský} and František {Kavička} and Josef {Štětina} and Bohumil {Sekanina} and Lubomír {Stránský},
  title="The effect of electromagnetic (i.e. induction) stirring of the melt of concast billets on the reduction of their surface defects",
  booktitle="Proceedings of ECF 17",
  year="2008",
  month="September",
  pages="196--196",
  publisher="VUTIUM Brno",
  address="Brno",
  isbn="9781617823190"
}