An influence of a triaxial stress applied perpendicularly to shear planes and shear direction during affine shear deformation of fcc crystals on the theoretical shear strength is studied for the (112)[111] shear system using first principles methods. Al crystal is used as the case study. The applied relaxation procedure guarantees that the crystal is subjected to a superposition of shear, normal and in-plane stresses with individually adjustable in-plane and normal stress values. The theoretical shear strength of aluminum increases under the applied compressive normal stress or tensile in-plane stresses and vice versa. Crystal relaxations during shear reflect bonding features of Al.

Vliv trojosého napětí působící kolmo na smykovou rovinu při afinní smykové deformaci FCC krystaly na teoretické smykové pevnosti je studována pro (112) [111] smyku systém s využitím prvních principů metod. Al krystal se používá jako případová studie. Použitá zaručuje uvolnění postup, že krystal se podrobí superpozicí smyk, normální a in-rovině zdůrazňuje, s individuálně nastavitelnou in-rovině a normální napětí hodnoty. Teoretická pevnost ve střihu z hliníku zvyšuje podle použité tlakové normální napětí nebo tahu in-rovině zdůrazňuje, a naopak. Krystal uvolnění při smyku odrážet lepení vlastnosti Al.

An influence of a triaxial stress applied perpendicularly to shear planes and shear direction during affine shear deformation of fcc crystals on the theoretical shear strength is studied for the (112)[111] shear system using first principles methods. Al crystal is used as the case study. The applied relaxation procedure guarantees that the crystal is subjected to a superposition of shear, normal and in-plane stresses with individually adjustable in-plane and normal stress values. The theoretical shear strength of aluminum increases under the applied compressive normal stress or tensile in-plane stresses and vice versa. Crystal relaxations during shear reflect bonding features of Al.

Ideální smyková pevnost, homodenní deformace, ab initio výpočty, fcc aluminium

Ideal shear strength, homogeneous deformation, ab initio calculations, fcc aluminum