Low cycle fatigue behaviour of ODS steels for nuclear application

KUBĚNA, I. KRUML, T. POLÁK, J. FOURNIER, B.

Czech title

Nízko cyklová únava ODS ocelí pro fúzní aplikace

English title

Low cycle fatigue behaviour of ODS steels for nuclear application

Type

journal article - other

Language

en

Original abstract

This study deals with the low cycle fatigue (LCF) behaviour of two steels strengthened by oxide dispersion. The ODS Eurofer steel shows cyclic softening, slower than in the case of the same steel without oxide particles. The 14Cr ODS ferritic steel is cyclically stable, even a slight cyclic hardening is observed at 650 degrees. The reasons for this different behaviour lie probably in the less resistant matrix with a lot of weak subgrain boundaries in ODS Eurofer, because no clear difference in the oxide particles distribution was found,

Czech abstract

Tato práce se zabívá nízkocyklovou únavou dvou ocelí zpevněních oxidickou dispersí. Ocel ODS Eurofer vykazuje cyklické změkčení, které je méně výrazné v porovnání se stejnou ocelí bez oxidických částic. Feritická 14Cr ODS ocel je cyklicky stabilní, dokonce bylo pozorováno cyklické zpevnění při zkoušce na teplotě 650 stupňů. Příčinou tohoto rozdílného chování je pravděpodobně méně odolná matrice s mnoha nízkoúhlovými hranicemi v oceli ODS Eurofer. Rozdíl v distribuci oxidických částic nebyl nalezen.

English abstract

This study deals with the low cycle fatigue (LCF) behaviour of two steels strengthened by oxide dispersion. The ODS Eurofer steel shows cyclic softening, slower than in the case of the same steel without oxide particles. The 14Cr ODS ferritic steel is cyclically stable, even a slight cyclic hardening is observed at 650 degrees. The reasons for this different behaviour lie probably in the less resistant matrix with a lot of weak subgrain boundaries in ODS Eurofer, because no clear difference in the oxide particles distribution was found,

Keywords in Czech

IV. generace jaderných reaktorů, fúzní energie, ODS oceli, nízkocyklová únava, cycklické změkčení

Keywords in English

Generation IV nuclear reactors; fusion energy; ODS steels; low cycle fatigue; cyclic softening

RIV year

2011

Released

01.03.2011

ISSN

1013-9826

Journal

Key Engineering Materials

Volume

2011

Number

465

Pages from–to

556–559

Pages count

4

BIBTEX


@article{BUT72496,
  author="Ivo {Kuběna} and Tomáš {Kruml} and Jaroslav {Polák} and Benjamin {Fournier},
  title="Low cycle fatigue behaviour of ODS steels for nuclear application",
  journal="Key Engineering Materials",
  year="2011",
  volume="2011",
  number="465",
  month="March",
  pages="556--559",
  issn="1013-9826"
}