Original abstract

The contribution deals with finite element analysis of stress state in subsized precracked threepoint bend specimen (KLST). A studied material was Eurofer97 steel. The true stress-true strain curve was obtained from tensile test. The threepoint bend tests were carried out on plain and sidegrooved specimens at ambient temperature and were simulated using ABAQUS 6.10. The stress state in KLST specimen was compared with the stress state of standard specimen. The analysis confirmed the stress state in KLST specimens at the crack tip does not correspond to conditions of standard fracture toughness determination because loss of constraint.

Czech abstract

Předložený příspěvek ze zabývá studiem stavu napjatosti v miniaturním tělese pro tříbodový ohyb (KSLT) pomocí MKP. Studovaným materiálem byla ocel Eurofer97. Nejprve byla v rámci experimentu provedena tahová zkouška a z ní pak získána zátěžná křivka oceli. Poté byly provedeny zkoušky tříbodovým ohybem za pokojové teploty na hladkých a bočně vrubovaných tělesech s předcyklovanou trhlinou a/W – 0,5, a/W – 0,35. Zkoušky byly modelovány prostřednictvím softwaru Abaqus 6.10. Napjatost v KLST tělesech byla modelově srovnána s napjatostí standardního a Charpyho tělesa používaných pro zkoušku tříbodovým ohybem. Pro daný materiál a podmínky testování nejsou v KLST tělesech dosahovány podmínky rovinné deformace. Použití bočních vrubů způsobuje, že je po tloušťce tělesa dosahováno stejné úrovně zatížení jako v jeho střední rovině. Maximální hodnota napjatosti ale zůstává stejná, jako u hladkého tělesa. Experimentálně a numericky určené hodnoty J integrálu byly ve vzájemné shodě do 6%.

English abstract

The contribution deals with finite element analysis of stress state in subsized precracked threepoint bend specimen (KLST). A studied material was Eurofer97 steel. The true stress-true strain curve was obtained from tensile test. The threepoint bend tests were carried out on plain and sidegrooved specimens at ambient temperature and were simulated using ABAQUS 6.10. The stress state in KLST specimen was compared with the stress state of standard specimen. The analysis confirmed the stress state in KLST specimens at the crack tip does not correspond to conditions of standard fracture toughness determination because loss of constraint.

Keywords in Czech

KLST, tříbodový ohyb, boční vruby, Eurofer97, J-integral

Keywords in English

KLST, three-point bending, side grooving, Eurofer97, J-integral

RIV year

2011

Released

18.04.2011

Publisher

Ústav fyziky materiálů AV ČR, v.v.i.

Location

Brno

ISBN

978-80-87434-03-1

Book

13th Conference Applied Mechanics 2011

Pages from–to

203–206

Pages count

4

BIBTEX


@inproceedings{BUT75860,
  author="Luděk {Stratil} and Vladislav {Kozák} and Hynek {Hadraba} and Ivo {Dlouhý},
  title="Stress state analysis of sub-sized pre-cracked three-point-bend specimen",
  booktitle="13th Conference Applied Mechanics 2011",
  year="2011",
  month="April",
  pages="203--206",
  publisher="Ústav fyziky materiálů AV ČR, v.v.i.",
  address="Brno",
  isbn="978-80-87434-03-1"
}