Publication detail

Low cycle response and fatigue life of aluminium alloy 7020 in the whole area of lifetime

ZAPLETAL, J. VANČURA, F. NĚMEC, K.

Czech title

Nízkocyklová odezva a únavová životnost slitiny hliníku 7020 v celé oblasti životnosti

English title

Low cycle response and fatigue life of aluminium alloy 7020 in the whole area of lifetime

Type

journal article - other

Language

en

Original abstract

In this article, cyclic hardening-softening behaviors of high strength aluminum alloy 7020 in T6 condition are studied. By comparison of cyclic deformation curve and unidirectional curve was found, that there is no significant change in cyclic response on tested material and that material can be accepted as cyclic stable. Experiments in high cycle area no discontinuity between low-cycle and high-cycle area was detected. Presented properties were not influenced by the different loading frequence (5 a 145 Hz) on different testing machines for low and high fatigue area.

Czech abstract

Článek se zabývá cyklickým zpevněním-změkčením vysoko pevnostní hliníkové slitiny 7020 ve stavu T6. V tomto článku , cyklické zpevnění – změkčení chování s vysokou pevnostní hliníkové slitiny 7020 T6 v stavu jsou studovány . Ve srovnání s cyklickou deformační křivky a křivka jednosměrné bylo zjištěno, že nedochází k významné změně v cyklické reakci na zkoušeného materiálu a že materiál může být přijaty jako stabilní cyklické . Experimenty ve vysokém cyklu plochu, která není diskontinuita mezi nízkým a vysokým cyklu cyklu oblasti nebyl zjištěn. Uvedené vlastnosti nebyly ovlivněny různými zatížení frekvence ( 5145 Hz) na různých zkušebních strojů pro nízké a vysoké únavy oblasti.

English abstract

In this article, cyclic hardening-softening behaviors of high strength aluminum alloy 7020 in T6 condition are studied. By comparison of cyclic deformation curve and unidirectional curve was found, that there is no significant change in cyclic response on tested material and that material can be accepted as cyclic stable. Experiments in high cycle area no discontinuity between low-cycle and high-cycle area was detected. Presented properties were not influenced by the different loading frequence (5 a 145 Hz) on different testing machines for low and high fatigue area.

Keywords in Czech

cyklické zpevnění-změkčení, mez únavy, Slitina hliníku 7020

Keywords in English

cyclic hardening-softening, fatigue limit, aluminium alloy 7020

RIV year

2010

Released

30.09.2010

ISSN

1210-0471

Volume

56

Number

2

Pages from–to

233–238

Pages count

6

BIBTEX


@article{BUT88917,
  author="Josef {Zapletal} and Filip {Vančura} and Karel {Němec},
  title="Low cycle response and fatigue life of aluminium alloy 7020 in the whole area of lifetime",
  year="2010",
  volume="56",
  number="2",
  month="September",
  pages="233--238",
  issn="1210-0471"
}