INVESTIGATION OF THE INFLUENCE OF ALTICRN COATING FOR DRY MILLING OF CONSTRUCTION STEEL 1.8159

JAROŠ, A. FIALA, Z. DVOŘÁČEK, J.

Czech title

VLIV POVLAKU ALTICRN PRO FRÉZOVÁNÍ OCELI 1.8159 BEZ POUŽITÍ PROCESNÍ KAPALINY

English title

INVESTIGATION OF THE INFLUENCE OF ALTICRN COATING FOR DRY MILLING OF CONSTRUCTION STEEL 1.8159

Type

conference paper

Language

en

Original abstract

This study deals with the benefits of very hard PVD coatings applied to the tools of high speed steels. The coating was synthesized by a cathodic-arc deposition process (CAE). The milling was carried out without using process liquid, so it was dry machining. During testing, cutting speed was varied (30; 35 and 40 m/min), but the feed per tooth (0.05 mm) and depth of cut (2 mm) were constant. The cutting tests were performed on vertical milling machine FV 25 CNC. The aim of this experiment was to compare the coated and uncoated HSSE-PM end mills and find out the benefits of coating AlTiCrN. The monitored parameters were force loading and flank wear. Best results were achieved by machining cutting speed 35m/min. Tools with PVD coating AlTiCrN had ten times longer durability than uncoated tools.

Czech abstract

Příspěvek pojednává o výhodách velmi tvrdých PVD povlaků používaných na nástroje z rychlořezných ocelí. Testovaným povlakem byl PVD povlak AlTiCrN, který byl na nástroj nanesen odpařováním pomocí elektrického oblouku. Povlaky na bázi Al se běžně používají pro frézování bez použití procesní kapaliny. Cílem experimentu bylo porovnání silového zatížení a opotřebení hřbetu u povlakovaných a nepovlakovaných HSS-PM fréz. Experiment probíhal na vertikální frézce FV 25 CNC. Po celou dobu experimentu byla konstantní šířka záběru ostří (2mm) a posuv na zub (0,05mm), proměnným vstupním parametrem byla pouze řezná rychlost (30; 35 a 40 m/min). Nejlepších výsledků bylo dosaženo při řezné rychlosti 35m/min, kde nástroj s AlTiCrN povlakem vydržel desetkrát více než nepovlakovaný nástroj (kritérium opotřebení VB=0,2mm).

English abstract

This study deals with the benefits of very hard PVD coatings applied to the tools of high speed steels. The coating was synthesized by a cathodic-arc deposition process (CAE). The milling was carried out without using process liquid, so it was dry machining. During testing, cutting speed was varied (30; 35 and 40 m/min), but the feed per tooth (0.05 mm) and depth of cut (2 mm) were constant. The cutting tests were performed on vertical milling machine FV 25 CNC. The aim of this experiment was to compare the coated and uncoated HSSE-PM end mills and find out the benefits of coating AlTiCrN. The monitored parameters were force loading and flank wear. Best results were achieved by machining cutting speed 35m/min. Tools with PVD coating AlTiCrN had ten times longer durability than uncoated tools.

Keywords in Czech

sílové zatížení, opotřebení hřbetu, rychlořezná ocel, PVD povlaky, čelní frézování

Keywords in English

force loading, flank wear, high-speed steel, PVD coatings, face milling

RIV year

2012

Released

17.12.2012

Publisher

MAGNANIMITAS

Location

Hradec Králové

ISBN

978-80-905243-3-0

Book

Sborník příspěvků Mezinárodní Masarykovy konference pro doktorandy a mladé vědecké pracovníky 2012

Edition number

3

Pages from–to

3475–3482

Pages count

7

BIBTEX


@inproceedings{BUT96579,
  author="Aleš {Jaroš} and Zdeněk {Fiala} and Jan {Dvořáček},
  title="INVESTIGATION OF THE INFLUENCE OF ALTICRN COATING FOR DRY MILLING OF CONSTRUCTION STEEL 1.8159",
  booktitle="Sborník příspěvků Mezinárodní Masarykovy konference pro doktorandy a mladé vědecké pracovníky 2012",
  year="2012",
  month="December",
  pages="3475--3482",
  publisher="MAGNANIMITAS",
  address="Hradec Králové",
  isbn="978-80-905243-3-0"
}