Originální abstrakt

Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment by Al-Si diffusion coating were cyclically strained under strain control at 800 degC in air. Changes in the shape and size of the superalloy precipitates during the surface treatment are documented. The structural and hardness characteristics of the hardened surface layer are presented. Hardening/softening curves, cyclic stress-strain curves, and fatigue life curves are obtained. The sections parallel to the specimen axis and fracture surfaces have been examined to study fatigue damage mechanisms. The coating results in fatigue life improvement while the stress response of the treated material is lower in comparison with the untreated one.

Český abstrakt

Práce se zabývá studiem vlivu vrstvy Al-Si na únavové chování (únavovou životnost) lité polykrystalické niklové superslitiny Inconel 713LC při vysoké teplotě 800 stC v režimu řízené deformace na vzduchu. Byly sledovány změny mikrostruktury, měřena tvrdost, dokumentovány křivky změkčení/zpevnění, cyklická napěťovo – deformační křivky, křivky únavové životnosti. Na základě lomových ploch a osových řezů byly také studovány mechanismy únavového poškození.

Anglický abstrakt

Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment by Al-Si diffusion coating were cyclically strained under strain control at 800 degC in air. Changes in the shape and size of the superalloy precipitates during the surface treatment are documented. The structural and hardness characteristics of the hardened surface layer are presented. Hardening/softening curves, cyclic stress-strain curves, and fatigue life curves are obtained. The sections parallel to the specimen axis and fracture surfaces have been examined to study fatigue damage mechanisms. The coating results in fatigue life improvement while the stress response of the treated material is lower in comparison with the untreated one.

Klíčová slova česky

Nízkocyklová únava, difúzní vrstva, Inconel 713LC, vysoká teplota, degradační mechanismy

Klíčová slova anglicky

Low cycle fatigue; diffusion coating; Inconel 713LC; high temperature; damage mechanisms;

Rok RIV

2010

Vydáno

15.03.2010

Nakladatel

Elsevier Ltd.

ISSN

1877-7058

Časopis

Procedia Engineering

Ročník

2

Číslo

1

Strany od–do

1983–1989

Počet stran

7

BIBTEX


@article{BUT48370,
  author="Martin {Juliš} and Karel {Obrtlík} and Simona {Hutařová} and Tomáš {Podrábský} and Jaroslav {Polák},
  title="Effect of Al-Si diffusion coating on the fatigue behavior of cast Inconel 713LC at 800 degC.",
  journal="Procedia Engineering",
  year="2010",
  volume="2",
  number="1",
  month="March",
  pages="1983--1989",
  publisher="Elsevier Ltd.",
  issn="1877-7058"
}