Studium počátečního únavového poškození v polykrystalech pomocí FIB techniky

MAN, J. WEIDNER, A. KUBĚNA, I. VYSTAVĚL, T. SKROTZKI, W. POLÁK, J.

Český název

Studium počátečního únavového poškození v polykrystalech pomocí FIB techniky

Anglický název

Application of FIB technique to study of early fatigue damage in polycrystals

Typ

článek v časopise - ostatní, Jost

Jazyk

en

Originální abstrakt

Focused ion beam (FIB) technique together with other advanced microscopic techniques were applied to study early microstructural changes leading to crack initiation in fatigued polycrystals. Dislocation structures of persistent slip bands (PSBs) and surrounding matrix were revealed in the bulk of surface grains by electron channelling contrast imaging (ECCI) technique on the FIB cross-sections. True shape of extrusions, intrusions and the path of initiated fatigue cracks were assessed in three dimensions by serial FIB cross-sectioning (FIB tomography). Advantageous potential of FIB technique and its other possible utilization in fatigue crack initiation studies in polycrystals are highlighted.

Český abstrakt

Technika fokusovaného iontového svazku spolu s dalšími pokročilými mikroskopickýmy technikami byla použita pro studium počátčních mikrostrukturních změn vedoucích k iniciaci trhlin v polykrystalu vystaveného cyklickému zatížení. Dislokační struktury perzistentích skluzových pásu a okoliní matrice byly pozorovány pomocí kanálového kontrastu (ECCI) a řezů připravených pomocí FIB techniky. Skutetčný tvar extruze a intruze byla stanovena pomocí FIB tomografie. Potenciál techniky FIB ve studiu inciace únavové trhliny je diskutován

Anglický abstrakt

Focused ion beam (FIB) technique together with other advanced microscopic techniques were applied to study early microstructural changes leading to crack initiation in fatigued polycrystals. Dislocation structures of persistent slip bands (PSBs) and surrounding matrix were revealed in the bulk of surface grains by electron channelling contrast imaging (ECCI) technique on the FIB cross-sections. True shape of extrusions, intrusions and the path of initiated fatigue cracks were assessed in three dimensions by serial FIB cross-sectioning (FIB tomography). Advantageous potential of FIB technique and its other possible utilization in fatigue crack initiation studies in polycrystals are highlighted.

Klíčová slova česky

fokusovaný iontový svazek, iniciace únavové trhliny, extruze, intruze

Klíčová slova anglicky

focused ion beam, fatigue crack initiation, extrusion, intrusion

Rok RIV

2010

Vydáno

09.08.2010

ISSN

1742-6588

Časopis

Journal of Physics: Conference Series

Ročník

240

Číslo

1

Strany od–do

1–4

Počet stran

4

BIBTEX


@article{BUT49784,
  author="Jiří {Man} and Anja {Weidner} and Ivo {Kuběna} and Tomáš {Vystavěl} and Werner {Skrotzki} and Jaroslav {Polák},
  title="Application of FIB technique to study of early fatigue damage in polycrystals",
  journal="Journal of Physics: Conference Series",
  year="2010",
  volume="240",
  number="1",
  month="August",
  pages="1--4",
  issn="1742-6588"
}