ZAPLETAL, J. VANČURA, F. NĚMEC, K.
Český název
Nízkocyklová odezva a únavová životnost slitiny hliníku 7020 v celé oblasti životnosti
Anglický název
Low cycle response and fatigue life of aluminium alloy 7020 in the whole area of lifetime
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
In this article, cyclic hardening-softening behaviors of high strength aluminum alloy 7020 in T6 condition are studied. By comparison of cyclic deformation curve and unidirectional curve was found, that there is no significant change in cyclic response on tested material and that material can be accepted as cyclic stable. Experiments in high cycle area no discontinuity between low-cycle and high-cycle area was detected. Presented properties were not influenced by the different loading frequence (5 a 145 Hz) on different testing machines for low and high fatigue area.
Český abstrakt
Článek se zabývá cyklickým zpevněním-změkčením vysoko pevnostní hliníkové slitiny 7020 ve stavu T6. V tomto článku , cyklické zpevnění – změkčení chování s vysokou pevnostní hliníkové slitiny 7020 T6 v stavu jsou studovány . Ve srovnání s cyklickou deformační křivky a křivka jednosměrné bylo zjištěno, že nedochází k významné změně v cyklické reakci na zkoušeného materiálu a že materiál může být přijaty jako stabilní cyklické . Experimenty ve vysokém cyklu plochu, která není diskontinuita mezi nízkým a vysokým cyklu cyklu oblasti nebyl zjištěn. Uvedené vlastnosti nebyly ovlivněny různými zatížení frekvence ( 5145 Hz) na různých zkušebních strojů pro nízké a vysoké únavy oblasti.
Anglický abstrakt
In this article, cyclic hardening-softening behaviors of high strength aluminum alloy 7020 in T6 condition are studied. By comparison of cyclic deformation curve and unidirectional curve was found, that there is no significant change in cyclic response on tested material and that material can be accepted as cyclic stable. Experiments in high cycle area no discontinuity between low-cycle and high-cycle area was detected. Presented properties were not influenced by the different loading frequence (5 a 145 Hz) on different testing machines for low and high fatigue area.
Klíčová slova česky
cyklické zpevnění-změkčení, mez únavy, Slitina hliníku 7020
Klíčová slova anglicky
cyclic hardening-softening, fatigue limit, aluminium alloy 7020
Rok RIV
2010
Vydáno
30.09.2010
ISSN
1210-0471
Ročník
56
Číslo
2
Strany od–do
233–238
Počet stran
6
BIBTEX
@article{BUT88917,
author="Josef {Zapletal} and Filip {Vančura} and Karel {Němec},
title="Low cycle response and fatigue life of aluminium alloy 7020 in the whole area of lifetime",
year="2010",
volume="56",
number="2",
month="September",
pages="233--238",
issn="1210-0471"
}