INFLUENCE OF THE CREEP ON THE STRUCTURE AND PROPERTIES OF THE CAST Ni-SUPERALLOY

PANTĚLEJEV, L. PODRÁBSKÝ, T. HRBÁČEK, K. HAKL, J. PETRENEC, M. NĚMEC, K.

Czech title

Vliv creepového zatěžování na strukturu a vlastnosti lité niklové superslitiny

English title

INFLUENCE OF THE CREEP ON THE STRUCTURE AND PROPERTIES OF THE CAST Ni-SUPERALLOY

Type

journal article - other

Language

en

Original abstract

During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods after the fracture of test bars.

Czech abstract

V provozních podmínkách spalovacích turbín proudových motorů jsou lopatky oběžných kol namáhány časově, teplotně a napěťově proměnnými cykly zatěžování. Během provozu jsou lopatky vystaveny řadě degradačních vlivů, zejména vysokoteplotní korozi, úna-vovým procesům a creepu. Creepovými zkouškami niklové superslitiny Inconel 713 LC při konstantním zatížení v rozsahu teplot 750 až 950C byly modelovány provozní podmínky žárových částí, používaných v plynových turbinách a turbokompresorech. Po lomu zkušebních tyčí byly metodami světelné a elektronové mikroskopie analyzovány změny ve struktuře v závislosti na době, teplotě a aplikovaném napětí.

English abstract

During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods after the fracture of test bars.

Keywords in Czech

Ni – superslitina, creep, mikrostruktura

Keywords in English

creep, Ni superalloy, microstructure

Released

28.04.2004

Publisher

Technical University of Košice

Location

Stará Lesná, Slovensko

ISSN

1335-1532

Journal

Acta Metallurgica Slovaca

Volume

10

Number

1

Pages count

5

BIBTEX


@article{BUT46414,
  author="Libor {Pantělejev} and Tomáš {Podrábský} and Karel {Hrbáček} and Jan {Hakl} and Martin {Petrenec} and Karel {Němec},
  title="INFLUENCE OF THE CREEP ON THE STRUCTURE AND PROPERTIES OF THE CAST Ni-SUPERALLOY",
  journal="Acta Metallurgica Slovaca",
  year="2004",
  volume="10",
  number="1",
  month="April",
  publisher="Technical University of Košice",
  address="Stará Lesná, Slovensko",
  issn="1335-1532"
}