INFLUENCE OF THE CREEP ON THE STRUCTURE AND PROPERTIES OF THE CAST Ni-SUPERALLOY
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods after the fracture of test bars.
Český abstrakt
V provozních podmínkách spalovacích turbín proudových motorů jsou lopatky oběžných kol namáhány časově, teplotně a napěťově proměnnými cykly zatěžování. Během provozu jsou lopatky vystaveny řadě degradačních vlivů, zejména vysokoteplotní korozi, úna-vovým procesům a creepu. Creepovými zkouškami niklové superslitiny Inconel 713 LC při konstantním zatížení v rozsahu teplot 750 až 950C byly modelovány provozní podmínky žárových částí, používaných v plynových turbinách a turbokompresorech. Po lomu zkušebních tyčí byly metodami světelné a elektronové mikroskopie analyzovány změny ve struktuře v závislosti na době, teplotě a aplikovaném napětí.
Anglický abstrakt
During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods after the fracture of test bars.
Klíčová slova česky
Ni – superslitina, creep, mikrostruktura
Klíčová slova anglicky
creep, Ni superalloy, microstructure
Vydáno
28.04.2004
Nakladatel
Technical University of Košice
Místo
Stará Lesná, Slovensko
ISSN
1335-1532
Časopis
Acta Metallurgica Slovaca
Ročník
10
Číslo
1
Počet stran
5
BIBTEX
@article{BUT46414,
author="Libor {Pantělejev} and Tomáš {Podrábský} and Karel {Hrbáček} and Jan {Hakl} and Martin {Petrenec} and Karel {Němec},
title="INFLUENCE OF THE CREEP ON THE STRUCTURE AND PROPERTIES OF THE CAST Ni-SUPERALLOY",
journal="Acta Metallurgica Slovaca",
year="2004",
volume="10",
number="1",
month="April",
publisher="Technical University of Košice",
address="Stará Lesná, Slovensko",
issn="1335-1532"
}