Slinování Al2O3 a ZrO2 nanokeramiky

DOBŠÁK, P. MACA, K. TRUNEC, M.

Český název

Slinování Al2O3 a ZrO2 nanokeramiky

Anglický název

Sintering of alumina and zirconia nanoceramics

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

The sintering and the microstructure of alumina and zirconia ceramics prepared by cold isostatic pressing of nanoceramic powders were studied. Ceramic powders contained 0, 1.5 and 3 mol.% of yttria. It was found that higher compacting pressures (700 MPa) yielded green bodies with smaller pores, which showed in their better sinterability. After sintering at 1100C, the bodies had a density exceeding 90% t.d. and grains below 80 nm. A critical ratio of the pore size in green bodies to the particle size was established, which enables sintering zirconia nanopowders of some 10 nm in size at a temperature of 1100C.

Český abstrakt

Bylo studováno slinování ZrO2 keramiky (dopované 0, 1,5 a 3mol.% Y2O3) připravené izostatickým lisováním nanometrických prášků. Vyšší lisovací tlak (700MPa) vedl ke keramickým polotovarům s menší velikostí pórů, které lépe slinovaly než tělesa lisovaná nižším tlakem (300MPa). Po slinování při 1100C měla tělesa hustotu vyšší než 99%t.h. a zrna menší než 80nm. Byl stanoven kritický poměr velikosti pórů a velikosti částic v keramickém polotovaru, který určuje která tělesa z prášku o velikosti 10nm budou slinovat při tepllotě 1100C.

Anglický abstrakt

The sintering and the microstructure of alumina and zirconia ceramics prepared by cold isostatic pressing of nanoceramic powders were studied. Ceramic powders contained 0, 1.5 and 3 mol.% of yttria. It was found that higher compacting pressures (700 MPa) yielded green bodies with smaller pores, which showed in their better sinterability. After sintering at 1100C, the bodies had a density exceeding 90% t.d. and grains below 80 nm. A critical ratio of the pore size in green bodies to the particle size was established, which enables sintering zirconia nanopowders of some 10 nm in size at a temperature of 1100C.

Klíčová slova anglicky

alumina,zirconia,nanoceramics, sintering

Rok RIV

2003

Vydáno

01.01.2003

Nakladatel

Faculty of Technology, University of Novi Sad

Místo

Novi Sad

ISBN

86-80995-46-0

Kniha

School of Ceramics, V Students' meeting

Počet stran

2

BIBTEX


@inproceedings{BUT11052,
  author="Petr {Dobšák} and Karel {Maca} and Martin {Trunec},
  title="Sintering of alumina and zirconia nanoceramics",
  booktitle="School of Ceramics, V Students' meeting",
  year="2003",
  month="January",
  publisher="Faculty of Technology, University of Novi Sad",
  address="Novi Sad",
  isbn="86-80995-46-0"
}