Výpočtová predikce trhlin tvaru v při vícechodém dopředném protlačování za studena
KUBÍK, P. PETRUŠKA, J. JUDAS, J. ŠEBEK, F.
Český název
Výpočtová predikce trhlin tvaru v při vícechodém dopředném protlačování za studena
Anglický název
Computational prediction of chevron cracking during multi-pass cold forward extrusion
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
The cold forward extrusion is a manufacturing process that is widespread in automated production due to its economic benefits. The cross-section is reduced during this process, which is accompanied by large plastic deformations. It may lead to the chevron cracking, which has to be predicted for flawless production and maintaining economic advantage. Therefore, the multi-pass cold forward extrusion of cylinder made from AISI 1045 was numerically simulated. The central cracks were predicted by the recently proposed uncoupled ductile fracture criteria. These were calibrated using various experiments, including the small punch test with additional fractographic observation. The material model was implemented into Abaqus using the user subroutine so that defects were successfully predicted using an element deletion technique.
Český abstrakt
Dopředné protlačování za studena je výrobní proces, který je rozšířený v automatizované produkci kvůli svým ekonomickým benefitům. Příčný průřez je při tomto procesu redukován, což je provázeno velkými plastickými deformacemi. To může vést ke vzniku trhlin tvaru v, které musí být predikovány pro výrobu bez vad a zachování ekonomické výhodnosti. Proto bylo numericky simulováno vícechodé dopředné protlačování válce z AISI 1045 za studena. Trhliny ve středu byly predikovány pomocí nedávno navržených nesvázaných kritérií tvárného porušování. Tato kritéria byla kalibrována pomocí různých experimentů zahrnujících miniaturní test protlačování s dodatečných fraktografickým pozorováním. Model materiálu byl implementován do Abaqusu pomocí uživatelské podprocedury tak, aby byly defekty úspěšně predikovány pomocí techniky mazání prvků.
Anglický abstrakt
The cold forward extrusion is a manufacturing process that is widespread in automated production due to its economic benefits. The cross-section is reduced during this process, which is accompanied by large plastic deformations. It may lead to the chevron cracking, which has to be predicted for flawless production and maintaining economic advantage. Therefore, the multi-pass cold forward extrusion of cylinder made from AISI 1045 was numerically simulated. The central cracks were predicted by the recently proposed uncoupled ductile fracture criteria. These were calibrated using various experiments, including the small punch test with additional fractographic observation. The material model was implemented into Abaqus using the user subroutine so that defects were successfully predicted using an element deletion technique.
Klíčová slova česky
Uhlíková ocel; praskání v centru; odříznutí; trhliny ve tvaru v; rentgen
Klíčová slova anglicky
Carbon steel; central bursting; cut-off; v-shaped cracks; x-ray
Vydáno
29.09.2023
ISSN
1526-6125
Ročník
102
Číslo
2023
Strany od–do
154–168
Počet stran
15
BIBTEX
@article{BUT184529,
author="Petr {Kubík} and Jindřich {Petruška} and Jakub {Judas} and František {Šebek},
title="Computational prediction of chevron cracking during multi-pass cold forward extrusion",
year="2023",
volume="102",
number="2023",
month="September",
pages="154--168",
issn="1526-6125"
}