Detail publikace

Creep nanostrukturního čistého niklu a jeho kompozitu připraveného elektrolytickým pokovováním

CIHLÁŘOVÁ, P. ŠVEJCAR, J.

Český název

Creep nanostrukturního čistého niklu a jeho kompozitu připraveného elektrolytickým pokovováním

Anglický název

Creep testing of electrodeposited nickel and its particle-reinforced nanocomposite

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

Nanocrystalline pure nickel and its particle-reinforced nanocomposite were produced by electrodeposition onto copper substrate under these conditions: direct current, 25 mA and 30 h. After electroplating, the copper substrate was metallographically ground out to obtain freestanding samples for the creep testing. The subject of study has been the evaluation of the creep characteristics of the electrodeposited unreinforced nickel and its nanocomposite reinforced by nano-sized SiO2 particles at temperatures in the range from 293 to 573 K. Fracture surfaces of the pure Ni and the composite after creep deformation were studied using SEM PHILIPS XL 30.

Český abstrakt

Nanostrukturní čistý nikl a jeho nanokompozit byly připraveny elektrolytickým pokovováním na měděném substrátu za těchto podmínek:stejnosměrný proud 25mA, 30hod. Měděná podložka byla mechanicky odstraněna a tím byl získán experimentální materiál pro mechanické a creepové zkoušky. Předmětem studia bylo srovnání tahových a creepových vlastností elektrolyticky nanášeného čistého niklu a jeho kompozitu s nanometrickými částicemi SiO2. Creepové zkoušky byly provedeny v rozsahu teplot od 293K do 473K. Experimentální materiál (Ni a Ni+SiO2) byl studován pomocí REM a TEM. Studium bylo především zaměřeno na rozložení částic SiO2 v matrici a velikost zrn matrice i částic.

Anglický abstrakt

Nanocrystalline pure nickel and its particle-reinforced nanocomposite were produced by electrodeposition onto copper substrate under these conditions: direct current, 25 mA and 30 h. After electroplating, the copper substrate was metallographically ground out to obtain freestanding samples for the creep testing. The subject of study has been the evaluation of the creep characteristics of the electrodeposited unreinforced nickel and its nanocomposite reinforced by nano-sized SiO2 particles at temperatures in the range from 293 to 573 K. Fracture surfaces of the pure Ni and the composite after creep deformation were studied using SEM PHILIPS XL 30.

Klíčová slova anglicky

nickel, nanomaterial, creep

Rok RIV

2006

Vydáno

01.11.2006

Nakladatel

VUT FSI v Brně

Místo

Brno

ISBN

80-214-3331-0

Kniha

Nano 06

Číslo edice

1

Strany od–do

277–280

Počet stran

4

BIBTEX


@inproceedings{BUT21669,
  author="Petra {Cihlářová} and Jiří {Švejcar},
  title="Creep testing of electrodeposited nickel and its particle-reinforced nanocomposite",
  booktitle="Nano 06",
  year="2006",
  month="November",
  pages="277--280",
  publisher="VUT FSI v Brně",
  address="Brno",
  isbn="80-214-3331-0"
}