The Influence of Sintering Schedule on Microstructure of SrTiO3 Ceramics

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

The influence of sintering schedule on the final microstructure of SrTiO3 ceramics was studied. From the point of view of reaching high final densities together with small grain size, pressure-assisted Spark Plasma Sintering was found as the most effective sintering method. In case of pressureless sintering heating schedules, Two Step Sintering method resulted in microstructures with higher density and smaller grain size than Constant Rate of Heating method.

Český abstrakt

Byl studován vliv slinovacího cyklu na mikrostrukturu SrTiO3 keramiky. Nejvyšších hustot a nejjemnější mikrostruktury bylo dosaženo metodou SPS, při beztlakém slinování se dvojstupňové slinování ukázalo jako efektivnější než konvenční jednostupňové slinování.

Anglický abstrakt

The influence of sintering schedule on the final microstructure of SrTiO3 ceramics was studied. From the point of view of reaching high final densities together with small grain size, pressure-assisted Spark Plasma Sintering was found as the most effective sintering method. In case of pressureless sintering heating schedules, Two Step Sintering method resulted in microstructures with higher density and smaller grain size than Constant Rate of Heating method.

Klíčová slova česky

SrTiO3, nanokeramika, slinování, mikrostruktura

Klíčová slova anglicky

SrTiO3, nanoceramics, sintering, microstructure

Vydáno

02.09.2007

Nakladatel

Verzal

Místo

Novi Sad, Serbia

Kniha

Proceedings of 3rd COST 539 Workshop: Nanostructured Materials: Processing and Applications

Strany od–do

46–47

Počet stran

2

BIBTEX


@inproceedings{BUT32937,
  author="Karel {Maca},
  title="The Influence of Sintering Schedule on Microstructure of SrTiO3 Ceramics",
  booktitle="Proceedings of 3rd COST 539 Workshop: Nanostructured Materials: Processing and Applications",
  year="2007",
  month="September",
  pages="46--47",
  publisher="Verzal",
  address="Novi Sad, Serbia"
}