Originální abstrakt

Thermal removal of polymer binder containing low-molecular-weight components from ceramic injection mouldings was studied. The effect of the shape and size of bodies on the process of binder removal was examined. Evaporation of low-molecular-weight components represented the most important process at the beginning of binder removal. It was found that a bed of activated carbon speed up removal of low-molecular-weight components. The mechanism of binder removal in a bed of activated carbon was described. Binder redistribution and evolution of porosity in the body during binder removal was investigated. A high rate of binder removal resulted in non-uniform binder distribution in the body. The formation of defects due to non-uniform binder removal was described and requirements for their elimination were proposed.

Český abstrakt

Bylo studováno tepelné odstraňování polymerního pojiva s obsahem nízkomolekulárních složek z keramických injekčně vstřikovaných výlisků. Byl zjišťován vliv tvaru a velikosti těles na průběh odstraňování pojiva. Vypařování složek s nízkou molekulovou hmotností představovalo nejdůležitější proces na počátku odstraňování pojiva. Byl popsán mechanismus odstraňování pojiva v zásypu aktivního uhlí, který umožnil zrychlit odstraňování pojiva. Bylo zkoumáno přerozdělování pojiva a vznik pórovitosti v tělese během odstraňování pojiva. Vysoká rychlost odstraňování pojiva způsobila nerovnoměrné rozdělení pojiva v tělese. Byl popsán vznik defektů způsobených nerovnoměrným odstraňováním pojiva a navržen způsob jejich eliminace.

Anglický abstrakt

Thermal removal of polymer binder containing low-molecular-weight components from ceramic injection mouldings was studied. The effect of the shape and size of bodies on the process of binder removal was examined. Evaporation of low-molecular-weight components represented the most important process at the beginning of binder removal. It was found that a bed of activated carbon speed up removal of low-molecular-weight components. The mechanism of binder removal in a bed of activated carbon was described. Binder redistribution and evolution of porosity in the body during binder removal was investigated. A high rate of binder removal resulted in non-uniform binder distribution in the body. The formation of defects due to non-uniform binder removal was described and requirements for their elimination were proposed.

Klíčová slova anglicky

Al2O3, Binder removal, Defects, Injection moulding, Porosity

Rok RIV

2002

Vydáno

15.08.2002

Nakladatel

Elsevier Science

ISSN

0955-2219

Časopis

Journal of the European Ceramic Society

Ročník

22

Číslo

13

Strany od–do

2231–2241

Počet stran

11

BIBTEX


@article{BUT40657,
  author="Martin {Trunec} and Jaroslav {Cihlář},
  title="Thermal removal of multicomponent binder from ceramic injection mouldings",
  journal="Journal of the European Ceramic Society",
  year="2002",
  volume="22",
  number="13",
  month="August",
  pages="2231--2241",
  publisher="Elsevier Science",
  issn="0955-2219"
}