Detail publikace

Oxidační přetavování vysokolegovaných ocelí Cr13Ni vháněním kyslíku

LEVÍČEK, P. STRÁNSKÝ, K. ŠENBERGER, J.

Český název

Oxidační přetavování vysokolegovaných ocelí Cr13Ni vháněním kyslíku

Anglický název

Oxydation re-melting of the Cr13Ni cast steel by means of oxygen-blowing

Typ

článek v časopise - ostatní, Jost

Jazyk

en

Originální abstrakt

Corrosion resistant 13% Cr and 1% Ni cast steel are used to produce castings for the Kaplan, Pelton and Francis turbines. These cast steels have also a satisfactory cavitation resistance. The oxidation re-melting process, where oxygen is blown into the bath, was elaborated in order to reduce the gas content (hydrogen and nitrogen) in re-melted corrosion-resistant 13% and 1% Ni steel scrap. This technology was tested on and elaborated for twenty-five melts, with special regard to oxygen-blowing conditions, mechanical properties (verified by the impact test) of the cast steel, and suppressing the formation of gas holes in the castings. Basic electric arc furnaces were used in the oxidation re-melting process of steel scrap.

Český abstrakt

Vysokolegované oceli odolné vůči korozi (Cr13Ni1) jsou nejčastěji používány na výrobu Kaplanových, Peltonových a Francisových turbín. Tyto lité oceli jsou také odolné vůči kavitaci. Oxidační přetavbou, kde je kyslík vháněn to tavící se lázně, se může redukovat množství plynů (vodíku a dusíku) z ocelového odpadu. Tato technologie byla laboratorně testována na 25 přetavbách a byly sledovány podmínky vhánění kyslíku, mechanické vlastnosti jednotlivých taveb a struktura materiálu (póry, staženiny). Na experiment byly vybrány elektrické pece.

Anglický abstrakt

Corrosion resistant 13% Cr and 1% Ni cast steel are used to produce castings for the Kaplan, Pelton and Francis turbines. These cast steels have also a satisfactory cavitation resistance. The oxidation re-melting process, where oxygen is blown into the bath, was elaborated in order to reduce the gas content (hydrogen and nitrogen) in re-melted corrosion-resistant 13% and 1% Ni steel scrap. This technology was tested on and elaborated for twenty-five melts, with special regard to oxygen-blowing conditions, mechanical properties (verified by the impact test) of the cast steel, and suppressing the formation of gas holes in the castings. Basic electric arc furnaces were used in the oxidation re-melting process of steel scrap.

Klíčová slova anglicky

Oxidation, turbines, Cr13Ni, oxygen-blowing

Vydáno

01.09.2003

Nakladatel

Stowarzyszenie techniczne odlewników Polskich

Místo

Zakopiańska 73 Kraków Poland

ISSN

0033-2275

Časopis

Przeglad Odlewnictwa

Ročník

2003

Číslo

9

Strany od–do

288–294

Počet stran

7

BIBTEX


@article{BUT46422,
  author="Petr {Levíček} and Karel {Stránský} and Jaroslav {Šenberger},
  title="Oxydation re-melting of the Cr13Ni cast steel by means of oxygen-blowing",
  journal="Przeglad Odlewnictwa",
  year="2003",
  volume="2003",
  number="9",
  month="September",
  pages="288--294",
  publisher="Stowarzyszenie techniczne odlewników Polskich",
  address="Zakopiańska 73
Kraków
Poland",
  issn="0033-2275"
}