Lokální aspekty šíření trhlin ve smykových módech v austenitické oceli
HOLÁŇ, L. POKLUDA, J. SLÁMEČKA, K.
Český název
Lokální aspekty šíření trhlin ve smykových módech v austenitické oceli
Anglický název
Local Aspects of Shear-Mode Crack Propagation in Austenitic Steel
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
An original and efficient testing setup has been designed in collaboration of the Institut of Physical Engineering and the Erich-Schmid Institute of Materials Science in Leoben. This device allows simultaneous fatigue crack propagation in pure shear modes II and III in a single specimen. The specimens were made of austenitic (x5NiCrTi26-15) steel and loaded under shear stress range from 80 MPa to 220 MPa with loading ratio R = 0.1. The stereophotogrammetrical reconstruction of the fracture surface morphology in the scanning electron microscope was performed. The analysis showed that the 3D topology of factory-roof patterns in torsion loading is very similar to that identified in the case of cyclic shear loading.
Český abstrakt
Originální testovací zařízení pro souběžné pozorování růstu trhlin ve smykových módech II a III bylo vyvinuto ve spolupráci ústavů Fyzikálního inženýrství a Ericha-Schmida v Leobenu, Rakousko. Studované vzorky byly vyrobeny z austenitické oceli a zatěžovány smykovými napětími v rozmezí 80 – 220 MPa při cyklickém poměru R = 0.1. Stereofotogrammetrická rekonstrukce lomových povrchů ukázala, že 3D topologie "factory roof" je velmi podobná morfologii při cyklickém krutu.
Anglický abstrakt
An original and efficient testing setup has been designed in collaboration of the Institut of Physical Engineering and the Erich-Schmid Institute of Materials Science in Leoben. This device allows simultaneous fatigue crack propagation in pure shear modes II and III in a single specimen. The specimens were made of austenitic (x5NiCrTi26-15) steel and loaded under shear stress range from 80 MPa to 220 MPa with loading ratio R = 0.1. The stereophotogrammetrical reconstruction of the fracture surface morphology in the scanning electron microscope was performed. The analysis showed that the 3D topology of factory-roof patterns in torsion loading is very similar to that identified in the case of cyclic shear loading.
Klíčová slova česky
smykové trhliny, lokální drsnost, rychlost růstu trhliny, mikromechanismy růstu, austenitická ocel
Klíčová slova anglicky
shear cracks, local roughness, crack growth rate, growth micromechanisms, austenitic steel
Rok RIV
2010
Vydáno
01.05.2010
ISSN
0009-2770
Časopis
Chemické listy
Ročník
104
Číslo
15
Strany od–do
314–317
Počet stran
4
BIBTEX
@article{BUT48104,
author="Libor {Holáň} and Jaroslav {Pokluda} and Karel {Slámečka},
title="Local Aspects of Shear-Mode Crack Propagation in Austenitic Steel",
journal="Chemické listy",
year="2010",
volume="104",
number="15",
month="May",
pages="314--317",
issn="0009-2770"
}