Detail publikace
Vyšší lomová houževnatost keramiky z tetragonálního oxidu zirkoničitého pomocí nanokrystalické struktury
TRUNEC, M. CHLUP, Z.
Český název
Vyšší lomová houževnatost keramiky z tetragonálního oxidu zirkoničitého pomocí nanokrystalické struktury
Anglický název
Higher fracture toughness of tetragonal zirconia ceramics through nanocrystalline structure
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
Fracture toughness of nanocrystalline zirconia ceramic stabilized with 1.5 mol.% Y2O3 was measured and compared with fracture toughness of submicrometer-grained zirconia ceramics stabilized with 3 mol.% Y2O3. It was found that nanocrystalline ceramics demonstrated higher fracture toughness than submicrometer-grained zirconia ceramics with both optimized and common grain sizes. The high fracture toughness of nanocrystalline zirconia was confirmed by two different testing methods: indentation method (15.5 MPa m0.5) and chevron notched beam method (7.9 MPa m0.5).
Český abstrakt
Byla změřena lomová houževnatost nanokrystalické keramiky z oxidu zirkoničitého stabilizovaného pomocí 1.5 mol.% Y2O3 a srovnána s lomovou houževnatostí keramiky s submikrometrovými zrny z oxidu zirkoničitého stabilizovaného pomocí 3 mol.% Y2O3. Bylo zjištěno, že nanokrystalická keramika vykazovala vyšší lomovou houževnatost než keramika s submikrometrovýni zrny, a to jak s optimalizovanou, tak i běžnou velikostí submikrometrových zrn. Vyšší lomová houževnatost nanokrystické keramiky z oxidu zirkoničitého byla potvrzena pomocí dvou různých testovacích metod: indentační metodou (15.5 MPa m0.5) a metodou "chevron notched beam" (7.9 MPa m0.5).
Anglický abstrakt
Fracture toughness of nanocrystalline zirconia ceramic stabilized with 1.5 mol.% Y2O3 was measured and compared with fracture toughness of submicrometer-grained zirconia ceramics stabilized with 3 mol.% Y2O3. It was found that nanocrystalline ceramics demonstrated higher fracture toughness than submicrometer-grained zirconia ceramics with both optimized and common grain sizes. The high fracture toughness of nanocrystalline zirconia was confirmed by two different testing methods: indentation method (15.5 MPa m0.5) and chevron notched beam method (7.9 MPa m0.5).
Klíčová slova česky
Oxid zirkoničitý, nanokrystalické materiály, hrubnutí, houževnatost, martenzitická fázová přeměna
Klíčová slova anglicky
Zirconia; Nanocrystalline materials; Coarsening; Toughness; Martensitic phase transformation
Rok RIV
2009
Vydáno
01.01.2009
Nakladatel
PERGAMON-ELSEVIER SCIENCE LTD
Místo
THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND
ISSN
1359-6462
Časopis
SCRIPTA MATERIALIA
Ročník
61
Číslo
1
Strany od–do
56–59
Počet stran
4
BIBTEX
@article{BUT48843,
author="Martin {Trunec} and Zdeněk {Chlup},
title="Higher fracture toughness of tetragonal zirconia ceramics through nanocrystalline structure",
journal="SCRIPTA MATERIALIA",
year="2009",
volume="61",
number="1",
month="January",
pages="56--59",
publisher="PERGAMON-ELSEVIER SCIENCE LTD",
address="THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND",
issn="1359-6462"
}