Kontrola metalurgie pomocí analýzy vměstků

ŠENBERGER, J. ZÁDĚRA, A. ČECH, J.

Český název

Kontrola metalurgie pomocí analýzy vměstků

Anglický název

Checking the metallurgy with the aid of inclusion analysis

Typ

článek v časopise - ostatní, Jost

Jazyk

en

Originální abstrakt

Results of studying the influence of inclusion morphology on properties of heavy casting are given. The inclusion morphology is dependent on content and kind of the deoxidizing element. Due to segregations the inclusions can be formed in heavy castings under different conditions (by concentration of deoxidizing elements) than in castings of common size. In heavy casting during deoxidation the inclusions of the IVth type occur more frequently. Deoxidation with zirconium shows to be for some heavy casting unsuitable one. Similarly in castings deoxidized with cerium and lanthanum the inclusions of greater sizes occur that can unfavourably influence the steel properties and increase the tendency to crack formation. The inclusion morphology after deoxidation with magnesium is also unsuitable for heavy castings.

Český abstrakt

Výsledky sledování vlivu morfologie vměstků na vlastnosti masivních odlitků. Morfologie vměstků je závislá na obsahu a druhu dezoxidačního prvku. V důsledku segregací mohou v masivních odlitcích vznikat vměstky za jiných podmínek (koncentrací dezoxidačních prvků) než v odlitcích běžné velikosti. Při dezoxidaci se v masivních odlitcích častěji vyskytují vměstky IV. typu. Dezoxidace zirkoniem se ukazuje pro některé masivní odlitky nevhodná. Podobě u odlitků dezoxidovaných cerem a lantanem se vyskytují vměstky větších rozměrů, které mohou nepříznivě ovlivnit vlastnosti oceli a zvýšit sklon ke vzniku trhlin. Rovněž morfologie vměsků po dezoxidaci hořčíkem je nevhodná pro masivní odlitky.

Anglický abstrakt

Results of studying the influence of inclusion morphology on properties of heavy casting are given. The inclusion morphology is dependent on content and kind of the deoxidizing element. Due to segregations the inclusions can be formed in heavy castings under different conditions (by concentration of deoxidizing elements) than in castings of common size. In heavy casting during deoxidation the inclusions of the IVth type occur more frequently. Deoxidation with zirconium shows to be for some heavy casting unsuitable one. Similarly in castings deoxidized with cerium and lanthanum the inclusions of greater sizes occur that can unfavourably influence the steel properties and increase the tendency to crack formation. The inclusion morphology after deoxidation with magnesium is also unsuitable for heavy castings.

Klíčová slova česky

Dezoxidace, masivní odlitky, morfologie vměstků

Klíčová slova anglicky

Deoxidation, heavy castings, morphology of inclusions

Rok RIV

2011

Vydáno

11.03.2011

ISSN

1897-3310

Ročník

11

Číslo

1

Strany od–do

118–122

Počet stran

5

BIBTEX


@article{BUT50795,
  author="Jaroslav {Šenberger} and Antonín {Záděra} and Jan {Čech},
  title="Checking the metallurgy with the aid of inclusion analysis",
  year="2011",
  volume="11",
  number="1",
  month="March",
  pages="118--122",
  issn="1897-3310"
}