Příprava transparentní nanokeramiky potlačením koalescence pórů

XIONG, Y. HU, J. SHEN, Z. POUCHLÝ, V. MACA, K.

Český název

Příprava transparentní nanokeramiky potlačením koalescence pórů

Anglický název

Preparation of Transparent Nanoceramics by Suppressing Pore Coalescence

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

en

Originální abstrakt

Microstructural developments in nanoceramics were investigated in 3Y-TZP compacts with relative density (RD) exceeding 93%. Special attentions were paid to the evolutions of pore structures. It was found that the densification process of nanoceramic compacts with apparently close porosity was greatly jeopardized by pore coalescence. This observation was interpreted by the coalescence of locally interconnected pores originated from inhomogeneous packing of particles. The pore coalescence can be suppressed by application of an external pressure. The processing principle was demonstrated by spark plasma sintering (SPS) with extended holding at a minimized sintering temperature. The highly dense 3Y-TZP nanoceramics containing no large pores became optically transparent

Český abstrakt

Byl studován vývoj mikrostruktury 3Y-TZP nanokeramiky s relativní hustotou větší než 93%. Speciální pozornost byla věnovány vývoji struktury pórů. Bylo zjištěno, že zhutňování nanokeramiky s uzavřenou pórovitostí bylo urychleno koalescencí pórů. To bylo vysvětleno koalescencí lokálně propojených pórů vzniklých z nehomogenit v tělese. Koalescenci pórů bylo možno potlačit aplikováním externího tlaku. Tento proces byl demonstrován pomocí aplikace Spark Plasma Sintering za použití nízkých teplot a dlouhých časů, což vedlo k získání optické transparence vzorků.

Anglický abstrakt

Microstructural developments in nanoceramics were investigated in 3Y-TZP compacts with relative density (RD) exceeding 93%. Special attentions were paid to the evolutions of pore structures. It was found that the densification process of nanoceramic compacts with apparently close porosity was greatly jeopardized by pore coalescence. This observation was interpreted by the coalescence of locally interconnected pores originated from inhomogeneous packing of particles. The pore coalescence can be suppressed by application of an external pressure. The processing principle was demonstrated by spark plasma sintering (SPS) with extended holding at a minimized sintering temperature. The highly dense 3Y-TZP nanoceramics containing no large pores became optically transparent

Klíčová slova česky

nanokeramika, ZrO2, SPS

Klíčová slova anglicky

nanoceramics, zirconia, spark plasma sintering

Rok RIV

2011

Vydáno

01.11.2011

Nakladatel

WILEY-BLACKWELL

Místo

COMMERCE PLACE, 350 MAIN ST, MALDEN 02148, MA, USA

ISSN

0002-7820

Ročník

94

Číslo

12

Strany od–do

4269–4273

Počet stran

5

BIBTEX


@article{BUT89661,
  author="Yan {Xiong} and Jianfeng {Hu} and Zhijian {Shen} and Václav {Pouchlý} and Karel {Maca},
  title="Preparation of Transparent Nanoceramics by Suppressing Pore Coalescence",
  year="2011",
  volume="94",
  number="12",
  month="November",
  pages="4269--4273",
  publisher="WILEY-BLACKWELL",
  address="COMMERCE PLACE, 350 MAIN ST, MALDEN 02148, MA,  USA",
  issn="0002-7820"
}