MIKROSTRUCTURAL CHANGES OF AIR PLASMA SPRAYED CoNiCrAlY COATING AFTER REMELTING
ŘIČÁNKOVÁ, V. ČELKO, L. KLAKURKOVÁ, L. ŠVEJCAR, J.
Český název
MIKROSTRUCTURAL CHANGES OF AIR PLASMA SPRAYED CoNiCrAlY COATING AFTER REMELTING
Anglický název
MIKROSTRUCTURAL CHANGES OF AIR PLASMA SPRAYED CoNiCrAlY COATING AFTER REMELTING
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
The samples in present study were prepared by air plasma spraying (APS) of CoNiCrAlY coatings onto the nickel-based superalloy INCONEL 713LC substrate surface. Immediately, after the spraying was onto the CoNiCrAlY coatings outer surface pressed an high purity aluminium sheet by means of uniaxial cold pressing techniue. After that the samples were annealed at the temperature of 650 C for different dwell-time in argon-flow atmosphere. The modified CoNiCrAlY coatings enriched by aluminium were produced. Moreover the voids, imperfectly melted powder particles, and oxide scale present in original plasma sprayed coating microstructure were eliminated. The scanning electron microscope (SEM) was used to record the modified coatings microstructure. Changes in chemical composition were studied by means of energy dispersive microanalysis (EDX).
Český abstrakt
V rámci této studie byly pozorovány změny v mikrostruktuře modifikovaného komerčně dostupného povlaku CoNiCrAlY připraveného pomocí technologie APS, s ohledem na jeho oxidační odolnost. Modifikace spočívala v sycení plazmou nanesených CoNiCrAlY povlaků hliníkem za jeho současného přetavování, které vedlo k eliminaci nežádoucího podílu oxidických vměstků v mikrostruktuře povlaku vyplývajícího z použité technologie jejich depozice. Cílem práce bylo především detailní pozorování vzájemných interakcí jednotlivých prvků a fázových transformací probíhajících v průběhu přípravy povlaků tohoto typu v průběžné ochranné argonové atmosféře v rozsahu teplot 650 C po dobu 0, 2, 5 hodin. Dále pak byly sledovány strukturní změny v průběhu modifikace původního povlaku způsobené objemovou difuzí reaktivních prvků. V konečném důsledku by tato modifikace komerčně dostupného povlaku CoNiCrAlY měla přispět ke zvýšení oxidační odolnosti tohoto typu povlaku.
Anglický abstrakt
The samples in present study were prepared by air plasma spraying (APS) of CoNiCrAlY coatings onto the nickel-based superalloy INCONEL 713LC substrate surface. Immediately, after the spraying was onto the CoNiCrAlY coatings outer surface pressed an high purity aluminium sheet by means of uniaxial cold pressing techniue. After that the samples were annealed at the temperature of 650 C for different dwell-time in argon-flow atmosphere. The modified CoNiCrAlY coatings enriched by aluminium were produced. Moreover the voids, imperfectly melted powder particles, and oxide scale present in original plasma sprayed coating microstructure were eliminated. The scanning electron microscope (SEM) was used to record the modified coatings microstructure. Changes in chemical composition were studied by means of energy dispersive microanalysis (EDX).
Klíčová slova česky
CoNiCrAlY; difuze; povrchové úpravy; intermetalika
Klíčová slova anglicky
M-CrAlY coatings, air plasma spraying, heat treatment, remelting, microstructure
Rok RIV
2012
Vydáno
25.05.2012
Nakladatel
TANGER Ltd.
Místo
Ostrava
ISBN
978-80-87294-29-1
Kniha
METAL 2012 Conference proceedings
Číslo edice
1
Strany od–do
442–447
Počet stran
6
BIBTEX
@inproceedings{BUT92143,
author="Veronika {Řičánková} and Ladislav {Čelko} and Lenka {Klakurková} and Jiří {Švejcar},
title="MIKROSTRUCTURAL CHANGES OF AIR PLASMA SPRAYED CoNiCrAlY COATING AFTER REMELTING",
booktitle="METAL 2012 Conference proceedings",
year="2012",
month="May",
pages="442--447",
publisher="TANGER Ltd.",
address="Ostrava",
isbn="978-80-87294-29-1"
}