Originální abstrakt
The contribution is focused on the assessment of the influence of the heat treatment of AZ61 magnesium alloy on its microstructure, mechanical properties and fatigue behaviour in both the low- and high-cycle regimes. Experimental material was manufactured by the squeeze casting method and the heat treatment was performed at a temperature of 380 C with various annealing time with subsequent water quenching. Optimal heat treatment conditions were established based on the results of tensile tests and metallographic analysis. Cyclic deformation behaviour and fatigue life of AZ61 magnesium alloys was studied under stress amplitude-control in a laboratory air at room temperature.
Český abstrakt
Příspěvek je zaměřen na hodnocení vlivu tepelného zpracování hořčíkové slitiny AZ61 na mikrostrukturu, mechanické vlastnosti a únavové chování v nízko a vysoko cyklové oblasti. Experimentální materiál byl vyroben metou squeeze casting a tepelně zpracován na teplotě 380 C s rozdílnou dobou výdrže s následným ochlazením do vody. Optimální podmínky pro tepelné zpracování byly stanoveny na základě výsledků zkoušek tahem a metalografické analýzy. Cyklická deformační odezva a únavová životnost hořčíkové slitiny AZ61 byla hodnocena v módu řízení zátěžné síly v laboratorních podmínkách.
Anglický abstrakt
The contribution is focused on the assessment of the influence of the heat treatment of AZ61 magnesium alloy on its microstructure, mechanical properties and fatigue behaviour in both the low- and high-cycle regimes. Experimental material was manufactured by the squeeze casting method and the heat treatment was performed at a temperature of 380 C with various annealing time with subsequent water quenching. Optimal heat treatment conditions were established based on the results of tensile tests and metallographic analysis. Cyclic deformation behaviour and fatigue life of AZ61 magnesium alloys was studied under stress amplitude-control in a laboratory air at room temperature.
Klíčová slova česky
AZ61, hořčíkové slitiny, rozpouštěcí žíhání, níkocyklová únava, vysokocyklová únava
Klíčová slova anglicky
AZ61, magnesium alloys, solution heat treatment, low cycle fatigue, high cycle fatigue
Rok RIV
2012
Vydáno
12.10.2012
Nakladatel
Technická univerzita Košice
Místo
Košice
ISSN
1335-1532
Ročník
18
Číslo
2
Strany od–do
92–99
Počet stran
9
BIBTEX
@article{BUT93222,
author="Josef {Zapletal} and Pavel {Doležal} and Pavel {Gejdoš} and Miroslava {Horynová},
title="INFLUENCE OF HEAT TREATMENT ON MICROSTRUCTURE AND FATIGUE BEHAVIOR OF AZ61 MAGNESIUM ALLOY",
year="2012",
volume="18",
number="2",
month="October",
pages="92--99",
publisher="Technická univerzita Košice",
address="Košice",
issn="1335-1532"
}