Vliv AlCr povlaku na nízkocyklové únavové chování lité niklové superslitiny při teplotě 800 C
OBRTLÍK, K. HUTAŘOVÁ, S. JULIŠ, M. PODRÁBSKÝ, T. KRUML, T.
Český název
Vliv AlCr povlaku na nízkocyklové únavové chování lité niklové superslitiny při teplotě 800 C
Anglický název
Influence of Al-Cr diffusion coating on low cycle fatigue behavior of cast nickel-base superalloy at 800 C
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
High temperature low cycle fatigue behavior of the cast nickel-based superalloy Inconel 713LC in as-received condition and coated with an Al-Cr diffusion layer have been investigated. The diffusion coating was deposited using the CVD out of pack technique. It was characterized and the hardness depth profile was measured. Fatigue tests were performed at 800 C in air using cylindrical specimens. Cyclic hardening/softening curves, cyclic stress-strain curve and fatigue life curves were obtained. The detrimental effect of the surface treatment on the Manson-Coffin and the derived Wöhler curves is documented. Fracture surface and surface relief observations and examinations of specimen sections help to discuss the effect of the diffusion coating on the fatigue life.
Český abstrakt
V příspěvku bylo studováno únavové chování lité niklové superslitiny Inconel 713LC v nízkocyklové oblasti za vysokých teplot. Únavové testy probíhaly za teplot 800 C na zkušebních tělesech ze základního materiálu a dále s aplikovaným povlakem AlCr. Difúzní bariéra AlCr byla vyrobena metodou CVD, technikou out of pack. V příspěvku je uveden tvrdostní profil povlaku, cyklické křivky zpevnění a změkčení, cyklické deformační křivky a křivky únavové živnotnosti. Byly rovněž studovány lomové plochy a únavové trhliny na osových řezech. Na základě výsledků lze konstatovat, že povlak AlCr má negativní vliv na únavovou životnost materiálu IN713LC v nízkocyklové oblasti.
Anglický abstrakt
High temperature low cycle fatigue behavior of the cast nickel-based superalloy Inconel 713LC in as-received condition and coated with an Al-Cr diffusion layer have been investigated. The diffusion coating was deposited using the CVD out of pack technique. It was characterized and the hardness depth profile was measured. Fatigue tests were performed at 800 C in air using cylindrical specimens. Cyclic hardening/softening curves, cyclic stress-strain curve and fatigue life curves were obtained. The detrimental effect of the surface treatment on the Manson-Coffin and the derived Wöhler curves is documented. Fracture surface and surface relief observations and examinations of specimen sections help to discuss the effect of the diffusion coating on the fatigue life.
Klíčová slova česky
Nízkocyklová únava, vysoké teploty, difúzní povlak, Inconel 713LC, cyklické křivky zpevnění a změkčení, cyklické deformační křivky, křivky únavové životnosti.
Klíčová slova anglicky
Low cycle fatigue, high temperature, diffusion coating, Inconel 713LC, cyclic hardening/softening curve, cyclic stress-strain curve, fatigue life curve, Knoop hardness.
Rok RIV
2012
Vydáno
26.08.2012
Nakladatel
Kazan
Místo
Russia
ISBN
978-5-905576-18-8
Kniha
19th European Conference on Fracture
Strany od–do
1–7
Počet stran
7
BIBTEX
@inproceedings{BUT96075,
author="Karel {Obrtlík} and Simona {Hutařová} and Martin {Juliš} and Tomáš {Podrábský} and Tomáš {Kruml},
title="Influence of Al-Cr diffusion coating on low cycle fatigue behavior of cast nickel-base superalloy at 800 C",
booktitle="19th European Conference on Fracture",
year="2012",
month="August",
pages="1--7",
publisher="Kazan",
address="Russia",
isbn="978-5-905576-18-8"
}