Detail publikace

Porovnání měření povrchu materiálu Inconel 713LC po únavových zkouškách metodami AFM a konfokální mikroskopií

ČELKO, L. POSPÍŠILOVÁ, S. JULIŠ, M. TOMANEC, O. PODRÁBSKÝ, T.

Český název

Porovnání měření povrchu materiálu Inconel 713LC po únavových zkouškách metodami AFM a konfokální mikroskopií

Anglický název

Comparison of INCONEL 713 LC surface measurements by AFM and Confocal microscopy after low cyclic fatigue test

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

INCONEL 713 LC is popular material for more exposed parts of turbine engines. These parts are usually exposured to high dynamic stress (fatigue processes, creep) and variable temperatures in corrosion environment (hot corrosion, oxidation and erosion). The most frequent failure of these parts is fatigue damage, which is started from inclusions at the surface. Topography of the surface of IN 713 LC in as received state and after low cycle fatigue tests at room temperature 23C and 800C was studied. Surface relief was formed by slip bands (intrusions and extrusions), which are generated by mechanism of microplastic deformation. Surface topography was measured by means of laser scanning confocal microscope LEXT OLS3000 (Olympus). Achieved results were compared with AFM Autoprobe (VEECO) and SEM (Philips XL30) measurements.

Český abstrakt

Inconel 713LC je velmi oblíbený materiál pro exponované součásti. Mezi degradační procesy vysokoteplotních součástí patří únavové procesy, creep, vysokoteplotní koroze, oxidace a eroze. Nejčastějšími příčinami poškození je právě únava, která se šíří inkluzemi z povrchu součásti. Topografie povrchu byla studována na výchozích vzorcích bez expozice a dále po nízkocyklovém únavovém testu za teplot 23C a 800C. Povrch byl studován metodami rastrovací konfokální mikroskopie, rastrovací elektronové mikroskopie a AFM.

Anglický abstrakt

INCONEL 713 LC is popular material for more exposed parts of turbine engines. These parts are usually exposured to high dynamic stress (fatigue processes, creep) and variable temperatures in corrosion environment (hot corrosion, oxidation and erosion). The most frequent failure of these parts is fatigue damage, which is started from inclusions at the surface. Topography of the surface of IN 713 LC in as received state and after low cycle fatigue tests at room temperature 23C and 800C was studied. Surface relief was formed by slip bands (intrusions and extrusions), which are generated by mechanism of microplastic deformation. Surface topography was measured by means of laser scanning confocal microscope LEXT OLS3000 (Olympus). Achieved results were compared with AFM Autoprobe (VEECO) and SEM (Philips XL30) measurements.

Klíčová slova anglicky

AFM, Confocal microscopy, fatique test

Rok RIV

2006

Vydáno

01.06.2006

Nakladatel

RMS Royal Microscopical Society

Místo

RMS Royal Microscopical Society, 37/38 St.Clements, Oxford OX4 IAJ, UK

Kniha

Microscience 2006

Číslo edice

1

Strany od–do

54–54

Počet stran

1

BIBTEX


@inproceedings{BUT19781,
  author="Ladislav {Čelko} and Simona {Hutařová} and Martin {Juliš} and Ondřej {Tomanec} and Tomáš {Podrábský},
  title="Comparison of INCONEL 713 LC surface measurements by AFM and Confocal microscopy after low cyclic fatigue test",
  booktitle="Microscience 2006",
  year="2006",
  month="June",
  pages="54--54",
  publisher="RMS Royal Microscopical Society",
  address="RMS Royal Microscopical Society, 37/38 St.Clements, Oxford OX4 IAJ, UK"
}